The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.
利用光学显微镜、扫描镜、能谱分析等试验手段对铝箔中"桔瓣"形针孔形成的原因进行了分析。
The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.
利用光学显微镜、扫描镜、能谱分析等试验手段对铝箔中"桔瓣"形针孔形成的原因进行了分析。
SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.
借助扫描镜观察
的叶片表面的钴微粒形核核心,通过能谱分析手段,
究型壳内表层的白色物质的相组成。
The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.
摘要针对日照2(
标﹟)锅炉屏式过热器泄漏进行了金相试验、晶间腐蚀倾向性试验和
镜能谱分析。
The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.
采用平板堆焊、高速摄影、波形分析、光学金相、扫描镜能谱分析等测试方法,
究了双层药皮对钛钙型不锈钢焊条气孔的影响。
声明:以例句、词性分类均由互联网资源自动生成,部分未经过人工审核,其表达内容亦不代表本软件的观点;若发现问题,欢迎向我们指正。
The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.
利用光学显微镜、扫描电镜、能谱分析等试验手对铝箔中"桔瓣"形针孔形成的原因进行了分析。
SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.
借助扫描电镜观察到细化的叶片表面的钴微粒形核核心,通过能谱分析手,
壳内表层的白色物质的相组成。
The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.
摘要针对日照电厂2(上标﹟)锅炉屏式过热器泄漏进行了金相试验、晶间腐蚀倾向性试验和电镜能谱分析。
The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.
采用平板堆焊、高速摄影、波形分析、光学金相、扫描电镜能谱分析等测试方法,了双层药皮对钛钙
不锈钢焊条气孔的影响。
声明:以上例句、词性分类均由互联网资源自动生成,部分未经过人工审核,其表达内容亦不代表本软件的观点;若发现问题,欢迎向我们指正。
The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.
利用光学显微镜、扫描电镜、析等试验手段对铝箔中"桔瓣"形针孔形成的原因进行了
析。
SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.
借助扫描电镜观察到细化的叶片面的钴微粒形核核心,通过
析手段,
究型壳
的白色物质的相组成。
The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.
摘要针对日照电厂2(上标﹟)锅炉屏式过热器泄漏进行了金相试验、晶间腐蚀倾向性试验和电镜析。
The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.
采用平板堆焊、高速摄影、波形析、光学金相、扫描电镜
析等测试方法,
究了双
药皮对钛钙型不锈钢焊条气孔的影响。
声明:以上例句、词性类均由互联网资源自动生成,部
未经过人工审核,其
达
容亦不代
本软件的观点;若发现问题,欢迎向我们指正。
The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.
利用光学显镜、扫描电镜、能谱分析等试验手段对铝箔中"桔瓣"形针孔形
的原因进行了分析。
SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.
借助扫描电镜观察到细化的叶片表面的形核核心,通过能谱分析手段,
究型壳内表层的白色物质的
。
The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.
摘要针对日照电厂2(上标﹟)锅炉屏式过热器泄漏进行了金试验、晶间腐蚀倾向性试验和电镜能谱分析。
The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.
采用平板堆焊、高速摄影、波形分析、光学金、扫描电镜能谱分析等测试方法,
究了双层药皮对钛钙型不锈钢焊条气孔的影响。
声明:以上例句、词性分类均由互联网资源自动生,部分未经过人工审核,其表达内容亦不代表本软件的观点;若发现问题,欢迎向我们指正。
The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.
利用光学显微镜、扫描电镜、能谱分析等试验手段对铝箔中""
针孔
成的原因进行了分析。
SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.
借助扫描电镜观察到细化的叶片表面的钴微粒核核心,通过能谱分析手段,
究型壳内表层的白色物质的相组成。
The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.
摘要针对日照电厂2(上标﹟)锅炉屏式过热器泄漏进行了金相试验、晶间腐性试验和电镜能谱分析。
The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.
采用平板堆焊、高速摄影、波分析、光学金相、扫描电镜能谱分析等测试方法,
究了双层药皮对钛钙型不锈钢焊条气孔的影响。
声明:以上例句、词性分类均由互联网资源自动生成,部分未经过人工审核,其表达内容亦不代表本软件的观点;若发现问题,欢迎我们指正。
The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.
利用光学显微镜、扫描电镜、能谱分析等试验手段对铝箔中"桔瓣"形针孔形成的行
分析。
SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.
借助扫描电镜观察到细化的叶片表面的钴微粒形核核心,通过能谱分析手段,究型壳内表层的白色物质的
组成。
The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.
摘要针对日照电厂2(上标﹟)锅炉屏式过热器泄漏行
试验、晶间腐蚀倾向性试验和电镜能谱分析。
The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.
采用平板堆焊、高速摄影、波形分析、光学、扫描电镜能谱分析等测试方法,
究
双层药皮对钛钙型不锈钢焊条气孔的影响。
声明:以上例句、词性分类均由互联网资源自动生成,部分未经过人工审核,其表达内容亦不代表本软件的观点;若发现问题,欢迎向我们指正。
The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.
利用光学显微镜、扫描镜、能谱分析等试验手段对铝箔中"桔瓣"形针孔形成
原因进行了分析。
SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.
借助扫描镜观察到
叶片表面
钴微粒形核核心,通过能谱分析手段,
究型壳内表层
白色物质
相组成。
The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.
摘要针对日2(上标﹟)锅炉屏式过热器泄漏进行了金相试验、晶间腐蚀倾向性试验和
镜能谱分析。
The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.
采用平板堆焊、高速摄影、波形分析、光学金相、扫描镜能谱分析等测试方法,
究了双层药皮对钛钙型不锈钢焊条气孔
影响。
声明:以上例句、词性分类均由互联网资源自动生成,部分未经过人工审核,其表达内容亦不代表本软件观点;若发现问题,欢迎向我们指正。
The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.
利用光学显微镜、扫描电镜、能谱分析等试验手段对铝箔中"桔瓣"形针孔形成的原因进行了分析。
SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.
借助扫描电镜细化的叶片表面的钴微粒形核核心,通过能谱分析手段,
究型壳内表层的白色物质的相组成。
The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.
摘要针对日照电厂2(﹟)
炉屏式过热器泄漏进行了金相试验、晶间腐蚀倾向性试验和电镜能谱分析。
The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.
采用平板堆焊、高速摄影、波形分析、光学金相、扫描电镜能谱分析等测试方法,究了双层药皮对钛钙型不锈钢焊条气孔的影响。
声明:以例句、词性分类均由互联网资源自动生成,部分未经过人工审核,其表达内容亦不代表本软件的
点;若发现问题,欢迎向我们指正。
The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.
利用光学显微镜、镜、能谱分析等试验手段对铝箔中"桔瓣"形针孔形成的原因进行了分析。
SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.
借助镜观察到细化的叶片表面的钴微粒形核核心,通过能谱分析手段,
究型壳内表层的白色物质的相组成。
The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.
摘要针对日照厂2(上标﹟)锅炉屏式过热器泄漏进行了金相试验、晶间腐蚀倾向性试验和
镜能谱分析。
The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.
采用平板、
速摄影、波形分析、光学金相、
镜能谱分析等测试方法,
究了双层药皮对钛钙型不锈钢
条气孔的影响。