Poly(vinyl alcohol)(PVA)-based polyanion was prepared by esterification of PVA with sulfuric acid.

硫酸与聚乙烯醇(PVA)经酯化制备PVA聚阴离子电解质。

Achieves the result of experiment to improve anionic dyes' dyeability on the fabrics with triethanolamine,polyethyleneglycol during finishing.

研究结果表明，整理液中添加三乙醇胺、聚乙二醇可大大提高阴离子染料对交联棉的可染。

C36CH2 cations have antiaromaticity with negative resonance energy, whereas C36CH2 anions have aromaticity with positive resonance energy.

反之，C36CH2阴离子因共振能为正值而具有较高的芳香。

Cast nylon modified with laurolactam was prepared by activated anionic copolymerization under the adiabatic condition.Its mechanical properties were studied.

在绝热条件下通过活化阴离子共聚制备十二内酰胺改浇铸尼龙,对其力学能进行了研究。

Some of the matrix have been aminated after the chlorome thylation of the copolymer giving an anion exchange resin.

部分共聚物经氯甲基化及季铵化后,制得强型阴离子交换树脂。

Finally,the most reasonable technological process of“stagewise grinding,coarse and fine classification,gravity separation magnetic separation reverse anionic flotation”has been found out.

最终推荐“阶段磨矿、粗细分级、重-磁-阴离子反浮选”为选矿合理工艺流程。

The auxiliary suspensibility of nonionics in seed clothing agent containing anionics or polysoap as main suspending agent was researched separately.

研究了非离子表面活分别在阴离子表面活高分子表面活作为主悬浮的种衣中的助悬。

We developed a new method to determine critical micella concentration of anionic surfactant by adsorption voltammetry, using neutral red, as a probe.

以易溶于有机溶，微溶于水的氧化-还原指示中红为探针，用吸附伏安法测了阴离子表面活的临界胶束浓度。

Furthermore, the crystal structure, surface characters of quartz and clinochlore, and the solution chemistry of oleic acid as the anionic collector were analyzed.

分析粉石英、斜绿泥石的晶体结构表面质以及油酸作阴离子捕收时的溶液化学。

Filler retention and drainability of wheat shaw pulp could be improved remarkably when PAC and PDADMAC were added as ATC before the addition of CPAM.

用PACPDADMAC作为阴离子捕捉可显著改善麦草浆的滤水，提高其留着率。

A process for decolourization of anionic dye containing wastewater by using waste plastics in the presence of cationic auxiliary and sodium dodecylbenzene sulfonate has been studied.

探讨了在阳离子助及十二烷基苯磺酸钠存在下,利用废旧塑料对阴离子染料的脱色工艺。

Anion in inhalable particulate matter can be completely dissolved in water by using ultrasonator and then measured by ion chromatography.Good accuracy and precision can be obtained.

介绍了用超声波振荡法能使可吸入颗粒物中的阴离子完全溶解在水中,然后用离子色谱法测,可获得良好的准确度精密度.

Polynionic celluloses were preparated by alkalify and etherify of refining cotton.The degree of replacement of the polynionic cellulosesis was high.The radicals of replacement were distributed evenly.

采用精制棉经过化、醚化得到高取代度且取代基均匀分布的聚阴离子纤维素产品。

Results indicate interestingly that the double bond of GMA polymerized with polystyryl carbanion and the molar ratio of epoxy end group and polystyrene oligomer can be adjusted.

在GMA与聚苯乙烯阴离子反应的过程中，GMA在活种的终端发生了聚合，所得产物中环氧端基与聚合产物的摩尔比可根据需要进行调节。

It has been proved that it is economical and feasible to eliminate educt alkali from coarse sodium tungstate with electrodialysis method of negative ion (1) selective membrane.

一价阴离子选择膜电渗析法从粗钨酸钠溶液中脱除游离是经济可行的。

Poly(vinyl alcohol)(PVA)-based polyanion was prepared by esterification of PVA with sulfuric acid.

硫酸与聚乙烯醇(PVA)经酯化制备PVA聚阴离子电解质。

Achieves the result of experiment to improve anionic dyes' dyeability on the fabrics with triethanolamine,polyethyleneglycol during finishing.

研究结果表明，整理液中添加三乙醇胺、聚乙二醇可大大提高阴离子染料对交联棉可染性。

C36CH2 cations have antiaromaticity with negative resonance energy, whereas C36CH2 anions have aromaticity with positive resonance energy.

反之，C36CH2阴离子因共振能为正值而具有较高芳香性和稳定性。

Cast nylon modified with laurolactam was prepared by activated anionic copolymerization under the adiabatic condition.Its mechanical properties were studied.

在绝热条件下通过活化阴离子共聚制备十二内酰胺改性浇铸尼龙,对其力学性能进行了研究。

Some of the matrix have been aminated after the chlorome thylation of the copolymer giving an anion exchange resin.

部分共聚物经氯甲基化及季铵化后,制得强型阴离子交换树脂。

Finally,the most reasonable technological process of“stagewise grinding,coarse and fine classification,gravity separation magnetic separation reverse anionic flotation”has been found out.

最终推荐“阶段磨矿、粗细分级、重-磁-阴离子反浮选”为选矿合理工艺流程。

The auxiliary suspensibility of nonionics in seed clothing agent containing anionics or polysoap as main suspending agent was researched separately.

研究了非离子表面活性剂分别在阴离子表面活性剂和高分子表面活性剂作为主悬浮剂种衣剂中助悬性。

We developed a new method to determine critical micella concentration of anionic surfactant by adsorption voltammetry, using neutral red, as a probe.

以易溶于有机溶剂，微溶于水氧化-还原指示剂中性红为探针，用吸附伏安法测定了阴离子表面活性剂临界胶束浓度。

Furthermore, the crystal structure, surface characters of quartz and clinochlore, and the solution chemistry of oleic acid as the anionic collector were analyzed.

分析粉英、斜绿晶体结构和表面性质以及油酸作阴离子捕收剂时溶液化学。

Filler retention and drainability of wheat shaw pulp could be improved remarkably when PAC and PDADMAC were added as ATC before the addition of CPAM.

用PAC和PDADMAC作为阴离子捕捉剂可显著改善麦草浆滤水性，提高其留着率。

A process for decolourization of anionic dye containing wastewater by using waste plastics in the presence of cationic auxiliary and sodium dodecylbenzene sulfonate has been studied.

探讨了在阳离子助剂及十二烷基苯磺酸钠存在下,利用废旧塑料对阴离子染料脱色工艺。

Anion in inhalable particulate matter can be completely dissolved in water by using ultrasonator and then measured by ion chromatography.Good accuracy and precision can be obtained.

介绍了用超声波振荡法能使可吸入颗粒物中阴离子完全溶解在水中,然后用离子色谱法测定,可获得良好准确度和精密度.

Polynionic celluloses were preparated by alkalify and etherify of refining cotton.The degree of replacement of the polynionic cellulosesis was high.The radicals of replacement were distributed evenly.

采用精制棉经过化、醚化得到高取代度且取代基均匀分布聚阴离子纤维素产品。

Results indicate interestingly that the double bond of GMA polymerized with polystyryl carbanion and the molar ratio of epoxy end group and polystyrene oligomer can be adjusted.

在GMA与聚苯乙烯阴离子反应过程中，GMA在活性种终端发生了聚合，所得产物中环氧端基与聚合产物摩尔比可根据需要进行调节。

It has been proved that it is economical and feasible to eliminate educt alkali from coarse sodium tungstate with electrodialysis method of negative ion (1) selective membrane.

一价阴离子选择膜电渗析法从粗钨酸钠溶液中脱除游离是经济可行。

Poly(vinyl alcohol)(PVA)-based polyanion was prepared by esterification of PVA with sulfuric acid.

硫酸与聚乙烯醇(PVA)经酯化制备PVA聚阴离电解质。

Achieves the result of experiment to improve anionic dyes' dyeability on the fabrics with triethanolamine,polyethyleneglycol during finishing.

研究结果表明，整理液中添加三乙醇胺、聚乙二醇可大大提阴离染料对交联棉的可染。

C36CH2 cations have antiaromaticity with negative resonance energy, whereas C36CH2 anions have aromaticity with positive resonance energy.

反之，C36CH2阴离因共振能为正值而具有较的芳稳定。

Cast nylon modified with laurolactam was prepared by activated anionic copolymerization under the adiabatic condition.Its mechanical properties were studied.

在绝热条件下通过活化阴离共聚制备十二内酰胺改浇铸尼龙,对其力学能进行了研究。

Some of the matrix have been aminated after the chlorome thylation of the copolymer giving an anion exchange resin.

部共聚物经氯甲基化及季铵化后,制得强型阴离交换树脂。

Finally,the most reasonable technological process of“stagewise grinding,coarse and fine classification,gravity separation magnetic separation reverse anionic flotation”has been found out.

最终推荐“阶段磨矿、粗细级、重-磁-阴离反浮选”为选矿合理工艺流程。

The auxiliary suspensibility of nonionics in seed clothing agent containing anionics or polysoap as main suspending agent was researched separately.

研究了非离表面活剂别在阴离表面活剂表面活剂作为主悬浮剂的种衣剂中的助悬。

We developed a new method to determine critical micella concentration of anionic surfactant by adsorption voltammetry, using neutral red, as a probe.

以易溶于有机溶剂，微溶于水的氧化-还原指示剂中红为探针，用吸附伏安法测定了阴离表面活剂的临界胶束浓度。

Furthermore, the crystal structure, surface characters of quartz and clinochlore, and the solution chemistry of oleic acid as the anionic collector were analyzed.

析粉石英、斜绿泥石的晶体结构表面质以及油酸作阴离捕收剂时的溶液化学。

Filler retention and drainability of wheat shaw pulp could be improved remarkably when PAC and PDADMAC were added as ATC before the addition of CPAM.

用PACPDADMAC作为阴离捕捉剂可显著改善麦草浆的滤水，提其留着率。

A process for decolourization of anionic dye containing wastewater by using waste plastics in the presence of cationic auxiliary and sodium dodecylbenzene sulfonate has been studied.

探讨了在阳离助剂及十二烷基苯磺酸钠存在下,利用废旧塑料对阴离染料的脱色工艺。

Anion in inhalable particulate matter can be completely dissolved in water by using ultrasonator and then measured by ion chromatography.Good accuracy and precision can be obtained.

介绍了用超声波振荡法能使可吸入颗粒物中的阴离完全溶解在水中,然后用离色谱法测定,可获得良好的准确度精密度.

Polynionic celluloses were preparated by alkalify and etherify of refining cotton.The degree of replacement of the polynionic cellulosesis was high.The radicals of replacement were distributed evenly.

采用精制棉经过化、醚化得到取代度且取代基均匀布的聚阴离纤维素产品。

Results indicate interestingly that the double bond of GMA polymerized with polystyryl carbanion and the molar ratio of epoxy end group and polystyrene oligomer can be adjusted.

在GMA与聚苯乙烯阴离反应的过程中，GMA在活种的终端发生了聚合，所得产物中环氧端基与聚合产物的摩尔比可根据需要进行调节。

It has been proved that it is economical and feasible to eliminate educt alkali from coarse sodium tungstate with electrodialysis method of negative ion (1) selective membrane.

一价阴离选择膜电渗析法从粗钨酸钠溶液中脱除游离是经济可行的。

Poly(vinyl alcohol)(PVA)-based polyanion was prepared by esterification of PVA with sulfuric acid.

硫酸与聚乙烯醇(PVA)经酯化制备PVA聚阴离子电解质。

Achieves the result of experiment to improve anionic dyes' dyeability on the fabrics with triethanolamine,polyethyleneglycol during finishing.

究结果表明，整理液中添加三乙醇胺、聚乙二醇可大大提高阴离子染料对交联棉的可染性。

C36CH2 cations have antiaromaticity with negative resonance energy, whereas C36CH2 anions have aromaticity with positive resonance energy.

反之，C36CH2阴离子因共振能为正值而具有较高的芳香性和稳定性。

Cast nylon modified with laurolactam was prepared by activated anionic copolymerization under the adiabatic condition.Its mechanical properties were studied.

在绝热条件下通过活化阴离子共聚制备十二内酰胺改性浇铸尼龙,对其力学性能进究。

Some of the matrix have been aminated after the chlorome thylation of the copolymer giving an anion exchange resin.

部分共聚物经氯甲基化及季铵化后,制得强型阴离子交换树脂。

Finally,the most reasonable technological process of“stagewise grinding,coarse and fine classification,gravity separation magnetic separation reverse anionic flotation”has been found out.

最终推荐“阶段磨矿、粗细分、--阴离子反浮选”为选矿合理工艺流程。

The auxiliary suspensibility of nonionics in seed clothing agent containing anionics or polysoap as main suspending agent was researched separately.

究非离子表面活性剂分别在阴离子表面活性剂和高分子表面活性剂作为主悬浮剂的种衣剂中的助悬性。

We developed a new method to determine critical micella concentration of anionic surfactant by adsorption voltammetry, using neutral red, as a probe.

以易溶于有机溶剂，微溶于水的氧化-还原指示剂中性红为探针，用吸附伏安法测定阴离子表面活性剂的临界胶束浓度。

Furthermore, the crystal structure, surface characters of quartz and clinochlore, and the solution chemistry of oleic acid as the anionic collector were analyzed.

分析粉石英、斜绿泥石的晶体结构和表面性质以及油酸作阴离子捕收剂时的溶液化学。

Filler retention and drainability of wheat shaw pulp could be improved remarkably when PAC and PDADMAC were added as ATC before the addition of CPAM.

用PAC和PDADMAC作为阴离子捕捉剂可显著改善麦草浆的滤水性，提高其留着率。

A process for decolourization of anionic dye containing wastewater by using waste plastics in the presence of cationic auxiliary and sodium dodecylbenzene sulfonate has been studied.

探讨在阳离子助剂及十二烷基苯磺酸钠存在下,利用废旧塑料对阴离子染料的脱色工艺。

Anion in inhalable particulate matter can be completely dissolved in water by using ultrasonator and then measured by ion chromatography.Good accuracy and precision can be obtained.

介绍用超声波振荡法能使可吸入颗粒物中的阴离子完全溶解在水中,然后用离子色谱法测定,可获得良好的准确度和精密度.

Polynionic celluloses were preparated by alkalify and etherify of refining cotton.The degree of replacement of the polynionic cellulosesis was high.The radicals of replacement were distributed evenly.

采用精制棉经过化、醚化得到高取代度且取代基均匀分布的聚阴离子纤维素产品。

Results indicate interestingly that the double bond of GMA polymerized with polystyryl carbanion and the molar ratio of epoxy end group and polystyrene oligomer can be adjusted.

在GMA与聚苯乙烯阴离子反应的过程中，GMA在活性种的终端发生聚合，所得产物中环氧端基与聚合产物的摩尔比可根据需要进调节。

It has been proved that it is economical and feasible to eliminate educt alkali from coarse sodium tungstate with electrodialysis method of negative ion (1) selective membrane.

一价阴离子选择膜电渗析法从粗钨酸钠溶液中脱除游离是经济可的。

Poly(vinyl alcohol)(PVA)-based polyanion was prepared by esterification of PVA with sulfuric acid.

硫酸与乙烯醇(PVA)经酯化制备PVA阴离电解质。

Achieves the result of experiment to improve anionic dyes' dyeability on the fabrics with triethanolamine,polyethyleneglycol during finishing.

研究结果明，整理液中添加三乙醇胺、乙二醇可大大提高阴离染料对交联棉的可染性。

C36CH2 cations have antiaromaticity with negative resonance energy, whereas C36CH2 anions have aromaticity with positive resonance energy.

反之，C36CH2阴离因振能为正值而具有较高的芳香性和稳定性。

Cast nylon modified with laurolactam was prepared by activated anionic copolymerization under the adiabatic condition.Its mechanical properties were studied.

在绝热条件下通过活化阴离制备十二内酰胺改性浇铸尼龙,对其力学性能进行了研究。

Some of the matrix have been aminated after the chlorome thylation of the copolymer giving an anion exchange resin.

部分物经氯甲基化及季铵化后,制得强型阴离交换树脂。

Finally,the most reasonable technological process of“stagewise grinding,coarse and fine classification,gravity separation magnetic separation reverse anionic flotation”has been found out.

最终推荐“阶段磨矿、粗细分级、重-磁-阴离反浮选”为选矿合理工艺流程。

The auxiliary suspensibility of nonionics in seed clothing agent containing anionics or polysoap as main suspending agent was researched separately.

研究了非离活性剂分别在阴离活性剂和高分活性剂作为主悬浮剂的种衣剂中的助悬性。

We developed a new method to determine critical micella concentration of anionic surfactant by adsorption voltammetry, using neutral red, as a probe.

以易溶于有机溶剂，微溶于水的氧化-还原指示剂中性红为探针，用吸附伏安法测定了阴离活性剂的临界胶束浓度。

Furthermore, the crystal structure, surface characters of quartz and clinochlore, and the solution chemistry of oleic acid as the anionic collector were analyzed.

分析粉石英、斜绿泥石的晶体结构和性质以及油酸作阴离捕收剂时的溶液化学。

Filler retention and drainability of wheat shaw pulp could be improved remarkably when PAC and PDADMAC were added as ATC before the addition of CPAM.

用PAC和PDADMAC作为阴离捕捉剂可显著改善麦草浆的滤水性，提高其留着率。

A process for decolourization of anionic dye containing wastewater by using waste plastics in the presence of cationic auxiliary and sodium dodecylbenzene sulfonate has been studied.

探讨了在阳离助剂及十二烷基苯磺酸钠存在下,利用废旧塑料对阴离染料的脱色工艺。

Anion in inhalable particulate matter can be completely dissolved in water by using ultrasonator and then measured by ion chromatography.Good accuracy and precision can be obtained.

介绍了用超声波振荡法能使可吸入颗粒物中的阴离完全溶解在水中,然后用离色谱法测定,可获得良好的准确度和精密度.

Polynionic celluloses were preparated by alkalify and etherify of refining cotton.The degree of replacement of the polynionic cellulosesis was high.The radicals of replacement were distributed evenly.

采用精制棉经过化、醚化得到高取代度且取代基均匀分布的阴离纤维素产品。

Results indicate interestingly that the double bond of GMA polymerized with polystyryl carbanion and the molar ratio of epoxy end group and polystyrene oligomer can be adjusted.

在GMA与苯乙烯阴离反应的过程中，GMA在活性种的终端发生了合，所得产物中环氧端基与合产物的摩尔比可根据需要进行调节。

It has been proved that it is economical and feasible to eliminate educt alkali from coarse sodium tungstate with electrodialysis method of negative ion (1) selective membrane.

一价阴离选择膜电渗析法从粗钨酸钠溶液中脱除游离是经济可行的。

Poly(vinyl alcohol)(PVA)-based polyanion was prepared by esterification of PVA with sulfuric acid.

硫酸与聚乙烯醇(PVA)经酯化制备PVA聚阴离子电解质。

Achieves the result of experiment to improve anionic dyes' dyeability on the fabrics with triethanolamine,polyethyleneglycol during finishing.

研究结果表明，整理液中添加三乙醇胺、聚乙二醇可大大提高阴离子染料对交联棉可染性。

C36CH2 cations have antiaromaticity with negative resonance energy, whereas C36CH2 anions have aromaticity with positive resonance energy.

反之，C36CH2阴离子因共振能为正值而具有较高芳香性和稳定性。

Cast nylon modified with laurolactam was prepared by activated anionic copolymerization under the adiabatic condition.Its mechanical properties were studied.

在绝热条件下通过活化阴离子共聚制备十二内酰胺改性浇铸尼龙,对其力学性能进行了研究。

Some of the matrix have been aminated after the chlorome thylation of the copolymer giving an anion exchange resin.

部分共聚物经氯甲基化及季铵化后,制得强型阴离子交换树脂。

Finally,the most reasonable technological process of“stagewise grinding,coarse and fine classification,gravity separation magnetic separation reverse anionic flotation”has been found out.

最终推荐“阶段磨矿、粗细分级、重-磁-阴离子反浮选”为选矿合理工艺流程。

The auxiliary suspensibility of nonionics in seed clothing agent containing anionics or polysoap as main suspending agent was researched separately.

研究了非离子表面活性剂分别在阴离子表面活性剂和高分子表面活性剂作为主悬浮剂种衣剂中助悬性。

We developed a new method to determine critical micella concentration of anionic surfactant by adsorption voltammetry, using neutral red, as a probe.

以易溶于有机溶剂，微溶于水氧化-还原指示剂中性红为探针，用吸附伏安法测定了阴离子表面活性剂临界胶束浓度。

Furthermore, the crystal structure, surface characters of quartz and clinochlore, and the solution chemistry of oleic acid as the anionic collector were analyzed.

分析粉英、斜绿晶体结构和表面性质以及油酸作阴离子捕收剂时溶液化学。

Filler retention and drainability of wheat shaw pulp could be improved remarkably when PAC and PDADMAC were added as ATC before the addition of CPAM.

用PAC和PDADMAC作为阴离子捕捉剂可显著改善麦草浆滤水性，提高其留着率。

A process for decolourization of anionic dye containing wastewater by using waste plastics in the presence of cationic auxiliary and sodium dodecylbenzene sulfonate has been studied.

探讨了在阳离子助剂及十二烷基苯磺酸钠存在下,利用废旧塑料对阴离子染料脱色工艺。

Anion in inhalable particulate matter can be completely dissolved in water by using ultrasonator and then measured by ion chromatography.Good accuracy and precision can be obtained.

介绍了用超声波振荡法能使可吸入颗粒物中阴离子完全溶解在水中,然后用离子色谱法测定,可获得良好准确度和精密度.

Polynionic celluloses were preparated by alkalify and etherify of refining cotton.The degree of replacement of the polynionic cellulosesis was high.The radicals of replacement were distributed evenly.

采用精制棉经过化、醚化得到高取代度且取代基均匀分布聚阴离子纤维素产品。

Results indicate interestingly that the double bond of GMA polymerized with polystyryl carbanion and the molar ratio of epoxy end group and polystyrene oligomer can be adjusted.

在GMA与聚苯乙烯阴离子反应过程中，GMA在活性种终端发生了聚合，所得产物中环氧端基与聚合产物摩尔比可根据需要进行调节。

It has been proved that it is economical and feasible to eliminate educt alkali from coarse sodium tungstate with electrodialysis method of negative ion (1) selective membrane.

一价阴离子选择膜电渗析法从粗钨酸钠溶液中脱除游离是经济可行。

Poly(vinyl alcohol)(PVA)-based polyanion was prepared by esterification of PVA with sulfuric acid.

硫酸与聚乙烯醇(PVA)经酯化制备PVA聚离子电解质。

Achieves the result of experiment to improve anionic dyes' dyeability on the fabrics with triethanolamine,polyethyleneglycol during finishing.

研表明，整理液中添加三乙醇胺、聚乙二醇可大大提高离子染料对交联棉的可染性。

C36CH2 cations have antiaromaticity with negative resonance energy, whereas C36CH2 anions have aromaticity with positive resonance energy.

反之，C36CH2离子因共振能为正值而具有较高的芳香性和稳性。

Cast nylon modified with laurolactam was prepared by activated anionic copolymerization under the adiabatic condition.Its mechanical properties were studied.

在绝热条件下通过活化离子共聚制备十二内酰胺改性浇铸尼龙,对其力学性能进行研。

Some of the matrix have been aminated after the chlorome thylation of the copolymer giving an anion exchange resin.

部分共聚物经氯甲基化及季铵化后,制得强型离子交换树脂。

Finally,the most reasonable technological process of“stagewise grinding,coarse and fine classification,gravity separation magnetic separation reverse anionic flotation”has been found out.

最终推荐“阶段磨矿、粗细分级、重-磁-离子反浮选”为选矿合理工艺流程。

The auxiliary suspensibility of nonionics in seed clothing agent containing anionics or polysoap as main suspending agent was researched separately.

研非离子表面活性剂分别在离子表面活性剂和高分子表面活性剂作为主悬浮剂的种衣剂中的助悬性。

We developed a new method to determine critical micella concentration of anionic surfactant by adsorption voltammetry, using neutral red, as a probe.

以易溶于有机溶剂，微溶于水的氧化-还原指示剂中性红为探针，用吸附伏安法测离子表面活性剂的临界胶束浓度。

Furthermore, the crystal structure, surface characters of quartz and clinochlore, and the solution chemistry of oleic acid as the anionic collector were analyzed.

分析粉石英、斜绿泥石的晶体构和表面性质以及油酸作离子捕收剂时的溶液化学。

Filler retention and drainability of wheat shaw pulp could be improved remarkably when PAC and PDADMAC were added as ATC before the addition of CPAM.

用PAC和PDADMAC作为离子捕捉剂可显著改善麦草浆的滤水性，提高其留着率。

A process for decolourization of anionic dye containing wastewater by using waste plastics in the presence of cationic auxiliary and sodium dodecylbenzene sulfonate has been studied.

探讨在阳离子助剂及十二烷基苯磺酸钠存在下,利用废旧塑料对离子染料的脱色工艺。

Anion in inhalable particulate matter can be completely dissolved in water by using ultrasonator and then measured by ion chromatography.Good accuracy and precision can be obtained.

介绍用超声波振荡法能使可吸入颗粒物中的离子完全溶解在水中,然后用离子色谱法测,可获得良好的准确度和精密度.

Polynionic celluloses were preparated by alkalify and etherify of refining cotton.The degree of replacement of the polynionic cellulosesis was high.The radicals of replacement were distributed evenly.

采用精制棉经过化、醚化得到高取代度且取代基均匀分布的聚离子纤维素产品。

Results indicate interestingly that the double bond of GMA polymerized with polystyryl carbanion and the molar ratio of epoxy end group and polystyrene oligomer can be adjusted.

在GMA与聚苯乙烯离子反应的过程中，GMA在活性种的终端发生聚合，所得产物中环氧端基与聚合产物的摩尔比可根据需要进行调节。

It has been proved that it is economical and feasible to eliminate educt alkali from coarse sodium tungstate with electrodialysis method of negative ion (1) selective membrane.

一价离子选择膜电渗析法从粗钨酸钠溶液中脱除游离是经济可行的。

Poly(vinyl alcohol)(PVA)-based polyanion was prepared by esterification of PVA with sulfuric acid.

硫酸与聚(PVA)经酯化制备PVA聚阴离子电解质。

Achieves the result of experiment to improve anionic dyes' dyeability on the fabrics with triethanolamine,polyethyleneglycol during finishing.

研究结果表明，整理液中添加三胺、聚二可大大提高阴离子染料对交联棉的可染性。

C36CH2 cations have antiaromaticity with negative resonance energy, whereas C36CH2 anions have aromaticity with positive resonance energy.

反之，C36CH2阴离子因共振能为正值而具有较高的芳香性和稳定性。

Cast nylon modified with laurolactam was prepared by activated anionic copolymerization under the adiabatic condition.Its mechanical properties were studied.

在绝热条件下通过活化阴离子共聚制备十二内酰胺改性浇铸尼龙,对其力学性能进行了研究。

Some of the matrix have been aminated after the chlorome thylation of the copolymer giving an anion exchange resin.

部共聚物经氯甲基化及季铵化后,制得强型阴离子交换树脂。

Finally,the most reasonable technological process of“stagewise grinding,coarse and fine classification,gravity separation magnetic separation reverse anionic flotation”has been found out.

最终推荐“阶段磨矿、粗细级、重-磁-阴离子反浮选”为选矿合理工艺流程。

The auxiliary suspensibility of nonionics in seed clothing agent containing anionics or polysoap as main suspending agent was researched separately.

研究了非离子表面活性剂别在阴离子表面活性剂和高子表面活性剂作为主悬浮剂的种衣剂中的助悬性。

We developed a new method to determine critical micella concentration of anionic surfactant by adsorption voltammetry, using neutral red, as a probe.

以易溶于有机溶剂，微溶于水的氧化-还原指示剂中性红为探针，用吸附伏安法测定了阴离子表面活性剂的临界胶束浓。

Furthermore, the crystal structure, surface characters of quartz and clinochlore, and the solution chemistry of oleic acid as the anionic collector were analyzed.

粉石英、斜绿泥石的晶体结构和表面性质以及油酸作阴离子捕收剂时的溶液化学。

Filler retention and drainability of wheat shaw pulp could be improved remarkably when PAC and PDADMAC were added as ATC before the addition of CPAM.

用PAC和PDADMAC作为阴离子捕捉剂可显著改善麦草浆的滤水性，提高其留着率。

A process for decolourization of anionic dye containing wastewater by using waste plastics in the presence of cationic auxiliary and sodium dodecylbenzene sulfonate has been studied.

探讨了在阳离子助剂及十二烷基苯磺酸钠存在下,利用废旧塑料对阴离子染料的脱色工艺。

Anion in inhalable particulate matter can be completely dissolved in water by using ultrasonator and then measured by ion chromatography.Good accuracy and precision can be obtained.

介绍了用超声波振荡法能使可吸入颗粒物中的阴离子完全溶解在水中,然后用离子色谱法测定,可获得良好的准确和精密.

Polynionic celluloses were preparated by alkalify and etherify of refining cotton.The degree of replacement of the polynionic cellulosesis was high.The radicals of replacement were distributed evenly.

采用精制棉经过化、醚化得到高取代且取代基均匀布的聚阴离子纤维素产品。

Results indicate interestingly that the double bond of GMA polymerized with polystyryl carbanion and the molar ratio of epoxy end group and polystyrene oligomer can be adjusted.

在GMA与聚苯阴离子反应的过程中，GMA在活性种的终端发生了聚合，所得产物中环氧端基与聚合产物的摩尔比可根据需要进行调节。

It has been proved that it is economical and feasible to eliminate educt alkali from coarse sodium tungstate with electrodialysis method of negative ion (1) selective membrane.

一价阴离子选择膜电渗法从粗钨酸钠溶液中脱除游离是经济可行的。

Poly(vinyl alcohol)(PVA)-based polyanion was prepared by esterification of PVA with sulfuric acid.

硫酸与聚乙烯醇(PVA)经酯制备PVA聚阴离电解质。

Achieves the result of experiment to improve anionic dyes' dyeability on the fabrics with triethanolamine,polyethyleneglycol during finishing.

研究结果表明，整理液中添加三乙醇胺、聚乙二醇可大大提高阴离染料对联棉的可染性。

C36CH2 cations have antiaromaticity with negative resonance energy, whereas C36CH2 anions have aromaticity with positive resonance energy.

反之，C36CH2阴离因共振能为正值而具有较高的芳香性和稳定性。

Cast nylon modified with laurolactam was prepared by activated anionic copolymerization under the adiabatic condition.Its mechanical properties were studied.

在绝热条件下通过活阴离共聚制备十二内酰胺改性浇铸尼龙,对其力学性能进行了研究。

Some of the matrix have been aminated after the chlorome thylation of the copolymer giving an anion exchange resin.

部分共聚物经氯甲基及季,制得强型阴离树脂。

Finally,the most reasonable technological process of“stagewise grinding,coarse and fine classification,gravity separation magnetic separation reverse anionic flotation”has been found out.

最终推荐“阶段磨矿、粗细分级、重-磁-阴离反浮选”为选矿合理工艺流程。

The auxiliary suspensibility of nonionics in seed clothing agent containing anionics or polysoap as main suspending agent was researched separately.

研究了非离表面活性剂分别在阴离表面活性剂和高分表面活性剂作为主悬浮剂的种衣剂中的助悬性。

We developed a new method to determine critical micella concentration of anionic surfactant by adsorption voltammetry, using neutral red, as a probe.

以易溶于有机溶剂，微溶于水的氧-还原指示剂中性红为探针，用吸附伏安法测定了阴离表面活性剂的临界胶束浓度。

Furthermore, the crystal structure, surface characters of quartz and clinochlore, and the solution chemistry of oleic acid as the anionic collector were analyzed.

分析粉石英、斜绿泥石的晶体结构和表面性质以及油酸作阴离捕收剂时的溶液学。

Filler retention and drainability of wheat shaw pulp could be improved remarkably when PAC and PDADMAC were added as ATC before the addition of CPAM.

用PAC和PDADMAC作为阴离捕捉剂可显著改善麦草浆的滤水性，提高其留着率。

A process for decolourization of anionic dye containing wastewater by using waste plastics in the presence of cationic auxiliary and sodium dodecylbenzene sulfonate has been studied.

探讨了在阳离助剂及十二烷基苯磺酸钠存在下,利用废旧塑料对阴离染料的脱色工艺。

Anion in inhalable particulate matter can be completely dissolved in water by using ultrasonator and then measured by ion chromatography.Good accuracy and precision can be obtained.

介绍了用超声波振荡法能使可吸入颗粒物中的阴离完全溶解在水中,然用离色谱法测定,可获得良好的准确度和精密度.

Polynionic celluloses were preparated by alkalify and etherify of refining cotton.The degree of replacement of the polynionic cellulosesis was high.The radicals of replacement were distributed evenly.

采用精制棉经过、醚得到高取代度且取代基均匀分布的聚阴离纤维素产品。

Results indicate interestingly that the double bond of GMA polymerized with polystyryl carbanion and the molar ratio of epoxy end group and polystyrene oligomer can be adjusted.

在GMA与聚苯乙烯阴离反应的过程中，GMA在活性种的终端发生了聚合，所得产物中环氧端基与聚合产物的摩尔比可根据需要进行调节。

It has been proved that it is economical and feasible to eliminate educt alkali from coarse sodium tungstate with electrodialysis method of negative ion (1) selective membrane.

一价阴离选择膜电渗析法从粗钨酸钠溶液中脱除游离是经济可行的。