SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.

借助扫描电镜观察到细化叶片表面钴微粒形核核心,通过能谱分手段,研究型壳内表层白色物质相组。

The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.

利用光学显微镜、扫描电镜、能谱分验手段对铝箔"桔瓣"形针孔形因进行了分。

The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.

摘要针对日照电厂2(上标﹟)锅炉屏式过热器泄漏进行了金相验、晶间腐蚀倾向性验和电镜能谱分。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄影、波形分、光学金相、扫描电镜能谱分测方法，研究了双层药皮对钛钙型不锈钢焊条气孔影响。

SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.

借助扫描电观察到细化的叶片表面的钴粒形核核心,通过能谱分析手段,研究型壳内表层的白色物质的相组成。

The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.

利用光学、扫描电、能谱分析等试验手段铝箔"桔瓣"形孔形成的原因进行了分析。

The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.

摘日照电厂2(上标﹟)锅炉屏式过热器泄漏进行了金相试验、晶间腐蚀倾向性试验和电能谱分析。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄影、波形分析、光学金相、扫描电能谱分析等测试方法，研究了双层药皮钛钙型不锈钢焊条气孔的影响。

SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.

借助扫描电镜观察到细化的叶片表面的钴微粒形核核心,通过能谱分析手段,研究型壳内表层的白色物质的相。

The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.

用光学显微镜、扫描电镜、能谱分析等试验手段对铝箔"桔瓣"形针孔形的原因进行了分析。

The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.

摘要针对日照电2(﹟)锅炉屏式过热器泄漏进行了金相试验、晶间腐蚀倾向性试验和电镜能谱分析。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄影、波形分析、光学金相、扫描电镜能谱分析等测试方法，研究了双层药皮对钛钙型不锈钢焊条气孔的影响。

SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.

借助镜观察到细化的叶片表面的钴微粒核核心,通过能谱分析手段,研究型壳内表层的白色物质的相组成。

The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.

利用光学显微镜、镜、能谱分析等试验手段对铝箔"桔瓣"针孔成的原因进行了分析。

The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.

摘要针对日照厂2(上标﹟)锅炉屏式过热器泄漏进行了金相试验、晶间腐蚀倾向性试验和镜能谱分析。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄、分析、光学金相、镜能谱分析等测试方法，研究了双层药皮对钛钙型不锈钢焊条气孔的响。

SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.

借助扫描镜观察到细化的叶片表面的钴微粒形核核心,通过能谱分析手段,研究型壳内表层的白色物质的相组成。

The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.

利显微镜、扫描镜、能谱分析等试验手段对铝箔"桔瓣"形针孔形成的原因进行了分析。

The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.

摘要针对厂2(上标﹟)锅炉屏式过热器泄漏进行了金相试验、晶间腐蚀倾向性试验和镜能谱分析。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采平板堆焊、高速摄影、波形分析、金相、扫描镜能谱分析等测试方法，研究了双层药皮对钛钙型不锈钢焊条气孔的影响。

SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.

借助镜观察到细化的叶片表面的钴微粒形核核心,通过能谱分析手段,研究型壳内表层的白色物质的相组成。

The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.

利用光学显微镜、镜、能谱分析等试验手段对铝箔"桔瓣"形针孔形成的原因进行了分析。

The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.

摘要针对日照厂2(上标﹟)锅炉屏式过热器泄漏进行了金相试验、晶间腐蚀倾向性试验和镜能谱分析。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄影、波形分析、光学金相、镜能谱分析等测试方法，研究了双层药皮对钛钙型不锈钢焊条气孔的影响。

SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.

借助扫描电镜观察到细化的叶片表面的钴微粒形核核心,通过能手段,研究型壳内表层的白色物质的相组成。

The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.

利用光学显微镜、扫描电镜、能等试验手段对铝箔"桔瓣"形针孔形成的原因进行了。

The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.

摘要针对日照电厂2(上标﹟)锅炉屏式过热器泄漏进行了金相试验、蚀倾向性试验和电镜能。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄影、波形、光学金相、扫描电镜能等测试方法，研究了双层药皮对钛钙型不锈钢焊条气孔的影响。

SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.

借助扫描镜观察到细化的叶片表面的钴微粒形核核心,通过能谱分析手段,研究型壳内表层的白色物质的相组。

The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.

光学显微镜、扫描镜、能谱分析等试验手段对铝箔"桔瓣"形针孔形的原因进行了分析。

The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.

摘要针对日照2(标﹟)锅炉屏式过热器泄漏进行了金相试验、晶间腐蚀倾向性试验和镜能谱分析。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采平板堆焊、高速摄影、波形分析、光学金相、扫描镜能谱分析等测试方法，研究了双层药皮对钛钙型不锈钢焊条气孔的影响。

SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.

借助扫描电镜观察到细化的叶片表面的钴微粒形,通过能谱分析手段,研究型壳内表层的白色物质的相组成。

The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.

利用光学显微镜、扫描电镜、能谱分析等手段对铝箔"桔瓣"形针孔形成的原因进行了分析。

The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.

摘要针对日照电厂2(上标﹟)锅炉屏式过热器泄漏进行了金相、晶间腐蚀倾向和电镜能谱分析。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄影、波形分析、光学金相、扫描电镜能谱分析等测方法，研究了双层药皮对钛钙型不锈钢焊条气孔的影响。